Green - 2.85mm HIPS Filament - 1 kg In stock
Free Shipping within Canada and the USA on Orders >$99 CAD
Local Pickup Available at our Hamilton, Ontario Store
- Tags
- 2.85mm , green , spo-disabled
SKU: StandardHIPS285Green1kg
High Impact Polystyrene (HIPS) is not only regarded as a good support filament, but it can work wonders as a standalone filament as well. Because of the fact that it is easy to print and does not warp.
It combines the hardness of polystyrene and elasticity of rubber to produce a tough thermoplastic which does not become brittle.
It is very similar to ABS, the only difference being that it is soluble in Limonene. This solution is easily obtained from the skin of lemons. Once the printing is complete, and the model has cooled, HIPS dissolves after being submerged for 24 hours, and the result is a print with clean, crisp overhanging. This makes it a great option as a support material when printing with ABS on a dual extrusion printer.
HIPS has been able to solve the issue of warping and deforming when the support material and printing material have different printing temperatures. Because HIPS share nearly identical printing temperature with ABS, it will lie together without any deformation or warping.
HIPS can be painted and handles sanding well. It can also be glued together by specialty adhesives.
Technical Data
| Product Description | |||
|---|---|---|---|
|
Main Characteristics
Applications:
Complies with:
|
|||
| General | |||
| Material Status | Commercial: Active | ||
| Literature 1 | Technical Datasheet | ||
| Availability | Asia Pacific | ||
| Features | Good Toughness | High Gloss | High Impact Resistance |
| Uses | Appliances | Business Equipment | Toys |
| Agency Ratings | FDA 21 CFR 177.1640 | ||
| Forms | Pellets | ||
| Processing Method | Compression Molding | Injection Molding | Sheet Extrusion |
| Physical | Nominal Value Unit | Test Method | |
| Specific Gravity -- -- |
1.04 g/cm³ ASTM D792 |
1030 kg/m³ ISO 11834 |
|
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.0 g/10 min | ASTM D1238 | |
| Melt volume-flow rate (200°C/5.0 kg) | 4.00 cm³/10min | ISO 11334 | |
| Molding Shrinkage - Flow | 0.40 to 0.70 % | ASTM D955 | |
| Mechanical | Nominal Value Unit | Test Method | |
| Tensile Modulus Compression Molded Injection Molded -- |
1750 MPa 1860 MPa 1770 MPa |
ASTM D638 ASTM D638 ISO 527-2 4 |
|
| Tensile Strength Yield, Compression Molded Yield, Injection Molded Yield Break, Compression Molded Break, Injection Molded |
20.7 MPa 22.8 MPa 25.0 MPa 14.5 MPa 19.3 MPa |
ASTM D638 ASTM D638 ISO 527-24 ASTM D638 ASTM D638 |
|
| Tensile Strain Yield Break, Compression Molded Break, Injection Molded |
1.5 % 30 % 50 % |
ISO 527-24 ASTM D638 ASTM D638 |
|
| Nominal strain at break | > 50 % | ISO 527-24 | |
| Flexural Modulus Compression Molded Injection Molded |
1900 MPa 2140 MPa |
ASTM D790 | |
| Flexural Strength Compression Molded Injection Molded |
38.3 MPa 44.8 MPa |
ASTM D790 | |
| Impact | Nominal Value Unit | Test Method | |
| Charpy notched impact strength -30°C 23°C |
4.00 kJ/m² 18.0 kJ/m² |
ISO 179/1eA4 | |
| Charpy impact strength -30°C 23°C |
60.0 kJ/m² 125 kJ/m² |
ISO 179/1eU4 | |
| Notched Izod Impact 23°C, Compression Molded 23°C, Injection Molded |
130 J/m 240 J/m |
ASTM D256 | |
| Gardner Impact (23°C) | 33.9 J | ASTM D3029 | |
| Thermal | Nominal Value Unit | Test Method | |
| Deflection Temperature Under Load 0.45 MPa 1.8 MPa, Unannealed 1.8 MPa, Annealed 1.8 MPa |
87.0°C 72.8°C 92.8°C 76.0°C |
ISO 75-24 ASTM D648 ASTM D648 ISO 75-24 |
|
| Vicat Softening Temperature -- 50°C/h, B (50N) |
102 °C 88.0 °C |
ASTM D1525 ISO 3064 |
|
| CLTE - Flow -- -- |
7.6E-5 cm/cm/°C 8.6E-5 cm/cm/°C |
ASTM D696 ISO 11359-24 |
|
| Flammability | Nominal Value Unit | Test Method | |
| Flame Rating5 (1.50 mm) | HB | UL 94 | |
| Burning Behav. at thickness h (3.10 mm, UL) | HB | ISO 12104 | |
| Optical | Nominal Value Unit | Test Method | |
| Gardner Gloss (60°) | 92 | ASTM D523 | |