Tangerine Orange - 1.75mm 3D Fuel Workday APLA Filament - 1kg
Advanced PLA (APLA) has higher heat resistance than ABS once it has gone through a simple annealing process. All you need is an oven or toaster oven! No warping, low/no odor, no heated bed necessary! If your 3D printer can print in standard PLA your mind will be blown with how easy it is to print with APLA. Standard PLA is nice to print, Advanced PLA is amazing to print with! APLA is the first 3D filament ever made from plastic that has been engineered and designed specifically with 3D printing in mind.
3D-Fuel Advanced PLA filament is being produced from high heat grade PLA, developed specifically for the manufacturing of 3D printer filament.
High heat grade resin exhibits improved heat resistance and has faster crystalization rates.
When using 3D-Fuel filament made from this resin you can expect:
- Low odor
- Higher print detail/resolution
- Excellent first layer adhesion
- Improved adhesion between layers
- Reduced warping, curling, and failed prints
It is essential to ensure filaments are dry prior to printing. Our filament will run best at an extrusion temperature of 190-230C. It is recommended to use high water content hair spray (as opposed to high ethyl alcohol content) or painter’s tape on the build plate to ensure the first layer of the print sticks to the plate. PEI (with a heated bed), BuildTak, and direct printing on acrylic can also produce good results.
For more stability and a higher quality print:
- Reduce the speed of the extruder to 30-60mm/second
- Increase infill to 30%
- Reduce layer height to 0.10mm
- For prints with curvatures, it is recommended to turn on rafts and supports in your settings.
- Print in an area with good airflow and/or and active cooling fan that directs airflow directly on the print.
- Clean the base plate after each day of printing.
- Clean the nozzle after every use for best performance.
Annealing (Heat Treating) Info
To get the maximum strength out of your 3D printed part, we recommend a post- annealing procedure that could be done in your oven at a range of 176-266F (80- 130C) to promote increased crystallization and further improve the heat deflection temperature.
For best results:
- Preheat the oven or toaster oven.
- Place print on room temperature baking sheet.
- Place baking sheet into oven/toaster oven.
- Wait 30-60 minutes for annealing to complete
- You may see the print take on a milky/matte/opaque color transformation.
- Turn the oven off.
- Wait for oven to cool before removing print.
Shrinkage and/or warping may occur. The degree of shrinkage/warping depends heavily on the part geometry.
|Physical Properties||APLA||ABS||Characteristic Effects|
|Clarity||Opaque||Opaque||Light Transmission of Part|
|Melting Point (°C)||165||105||Polymer melting temperature|
|Diameter Tolerances (mm)||±.05||±.05||Variation of filament size|
|Ovality(mm)||±.04||±.04||Difference between two diameters measured across the filament's profile|
|Density (g/cm2)||1.24||1.04||Density of filament material|
|Melt Flow Index (195°C)||11||2||Viscosity of filament in molten state|
|Tensile Strength at Yield (MPa)||55||33||The force required to deform|
|Tensile Elongation (%)||2.85||2.98||The amount of stretching before breaking|
|Tensile Modulus (MPa)||2904||1920||The rigidity or resistance to stretching|
|Toughness (J)||0.19||0.12||The amount of energy to break|
|Heat Deformation Temp (°C)||144||98||Temp at which it will begin to deform after being post annealed|
|Volatile Compounds Detected||5||35||Number of identified compounds released during 3D printing|
|Volatiles with Toxicity Concerns||0||11||Number of identified compounds with a toxic health rating according to GHS|