Golden - 1.75mm ABS Filament - 1 kg Out of stock
Free Shipping within Canada and the USA on Orders >$99 CAD
Shipping via UPS to major cities and Canada Post for rural areas.
Average delivery time to Ontario and Quebec is 1 business day!
- Tags
- 1.75mm , gold , metallic , spo-disabled
SKU: StandardABS175Golden1kg
ABS (Acrylonitrile Butadiene Styrene) is the grandfather of home 3D printing filaments. For best results, ABS requires a heated bed and preferably an enclosed printing environment.
ABS has a higher resistance to heat and starts to soften at around 105º C. For this reason, 3D printed objects used in outdoor or higher heat applications tend to stand up better when printed from ABS Filament.
One of the downsides to printing with ABS is the strong smell while it prints. While it doesn’t bother most people, some people may have issues with printing with ABS in confined spaces. We recommend printing in a well ventilated room.
| Physical | Nominal Value Unit | Test Method |
|---|---|---|
| Specific Gravity -- 23°C |
1.05 g/cm³ 1.05 g/cm³ |
ASTM D792 ISO 1183 |
| Melt Mass-Flow Rate (MFR) 200°C/5.0 kg 220°C/10.0 kg |
1.6 g/10 min 22 g/10 min |
ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 22.0 cm³/10min | ISO 1133 |
| Mechanical | Nominal Value Unit | Test Method |
| Tensile Stress Yield Break 3.00 mm4 |
54.0 MPa 37.0 MPa 45.1 MPa |
ISO 527-2/50 ISO 527-2/50 ASTM D638 |
| Tensile Elongation Break, 3.00 mm4 Break |
25 % 20 % |
ASTM D638 ISO 527-2/50 |
| Flexural Modulus 6.00 mm5 --6 |
2650 MPa 2200 MPa |
ASTM D790 ISO 178 |
| Flexural Strength 6.00 mm5 --6 |
77.5 MPa 76.0 MPa |
ASTM D790 ISO 178 |
| Impact | Nominal Value Unit | Test Method |
| Charpy Notched Impact Strength | 20 kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | ISO 179 |
| Notched Izod Impact 23°C, 3.00 mm 23°C, 6.00 mm -- |
210 J/m 180 J/m 18 kJ/m² |
ASTM D256 ASTM D256 ISO 180/1A |
| Unnotched Izod Impact Strength | 60 kJ/m² | ISO 180/1U |
| Hardness | Nominal Value Unit | Test Method |
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Ball Indentation Hardness (H 358/30) | 110 MPa | ISO 2039-1 |
| Thermal | Nominal Value Unit | Test Method |
| Deflection Temperature Under Load 1.8 MPa, Unannealed 1.8 MPa, Unannealed 1.8 MPa, Annealed 1.8 MPa, Annealed |
85.0°C 88.0°C 95.0°C 98.0°C |
ASTM D648 ISO 75-2/A ASTM D648 ISO 75-2/A |
| Vicat Softening Temperature -- -- -- |
105°C 104°C 100°C |
ASTM D1525 7 ISO 306/A50 ISO 306/B50 |
| Flammability | Nominal Value Unit | Test Method |
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value Unit | |
| Drying Temperature | 80.0 to 85.0 °C | |
| Drying Time | 2.0 to 4.0 hr | |
| Rear Temperature | 180 to 220 °C | |
| Middle Temperature | 190 to 230 °C | |
| Front Temperature | 190 to 230 °C | |
| Mold Temperature | 30.0 to 70.0 °C | |