Blue - 1.75mm TPU Filament - 1 kg
In stockClick here to read our Price Match Policy.
Thermoplastic polyurethane has a famous ancestor which it gets more commonly confused with, TPE filament. But this newer version is entirely different from its predecessor as it has higher abrasion resistance, greater chemical resistance, and lower shrinkage.
It is a serious multiuse flexible filament which has excellent layer adhesion.
TPU’s resistance to grease, oil, and solvents making it more useful for industrial applications such as medical devices, power tools, automotive instrument panels, drive belts, caster wheels, footwear, inflatable rafts and mobile phone cases.
It creates rubbery elastic parts, and the less amount of infill you use the more flexible your finished object will be. So, your end print will be a super stretchable object that PLA and ABS cannot print ever.
TPU also has a considerably lower shrinkage as compared to its ancestor TPE, so if you require accurate measurements post printing, it is wiser to stick with TPU. It is also UV resistant and has a better retention of its elastic properties at a lower temperature and higher print resolution than TPE, so it is more suited to making mechanical parts.
It works wonders with printers with two heads since TPU can add that additional layer of the rigid base material to create a soft surface.
Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties, outstanding wear resistance, good tensile strength, good damping and resilience performance and superior low temperature flexibility.
Sport-shoe soles and accessories, Skiboot shells, technical mouldings, e.g. seals, castor tyres, tubing.
|Material Status||Commercial: Active|
|Literature1||Processing - Elastollan (English)
Technical Datasheet (English)
|Features||Good Wear Resistance||Low Temperature Flexibility||Resilient|
|Processing Method||Blow Molding||Extrusion||Injection Molding|
|Physical||Nominal Value Unit||Test Method|
|Density||1.21 g/cm³||ISO 1183/A|
|Mechanical||Nominal Value Unit||Test Method|
|Abrasion Loss||30.0 mm³||ISO 4649-A|
|Elastomers||Nominal Value Unit||Test Method|
|Tensile Elongation 3 (Break)||550 %||DIN 53504|
|Tear Strength 4||90 kN/m||ISO 34-1|
23°C, 72 hr
70°C, 24 hr
|Impact||Nominal Value Unit||Test Method|
|Charpy Notched Impact Strength
|Hardness||Nominal Value Unit||Test Method|
Shore A, 3 sec
Shore D, 3 sec
|Injection||Nominal Value Unit|
|Processing (Melt) Temp||190 to 220 °C|
|Mold Temperature||20.0 to 50.0 °C|
|Extrusion||Nominal Value Unit|
|Melt Temperature||180 to 230 °C|