Henkel LOCTITE 3D 3843 Matte Black
The Henkel/Loctite 3D Resin 3843 in Matte Black is a premium choice for professionals and enthusiasts in the realm of 3D printing. This 1KG resin offers a unique blend of high toughness and moderate temperature resistance, making it suitable for a wide array of applications.
Key Features:
- Toughness and Flexibility: The semi-flexible nature of the resin, combined with its moderate temperature resistance (HDT 60° C), ensures durability and adaptability for various uses.
- Superior Strength and Impact Resistance: Engineered for high impact strength, this resin is perfect for creating strong, durable parts with an outstanding surface finish.
- Versatile Applications: Ideal for functional prototyping, manufacturing aids, jigs & fixtures, housing, covers, and insoles. Its versatility makes it suitable for a broad range of industrial and creative projects.
- High-Quality Finish: The matte black color provides an excellent surface finish, enhancing the aesthetic appeal of the printed objects.
- Compatibility: This resin is compatible with a range of DLP 3D printers, including EnvisionTEC, Stratasys, RapidShape, Photocentric, Zortrax, Fortify, Genera, Prusa, Sisma, and Asiga models.
Technical Specifications:
- Volume: 1kg
- Viscosity: 720-870 cP
- Density: 1.18 g/cm³ (solid), 1.07 g/cm³ (liquid)
- Surface Hardness: 75 Shore D
- Tensile Stress at Break: 51 ± 2 MPa
- Young’s Modulus: 1806 ± 47 MPa
- Elongation at Break (EAB): 43 ± 10%
- IZOD Impact (Notched): 53 ± 4 J/m
Safety and Storage:
Store in a dark and room-temperature environment. Always use protective gloves when handling the resin.
Biocompatibility:
Irritation certified according to ISO10993-23, making it safe for various applications.
Properties
| Mechanical Properties | Measure | Method | Green | Post Processed |
| Young's Modulus | MPa | ASTM D638 | 703-883[1] | 1630-1990[16,2] |
| Tensile Stress at Break | MPa | ASTM D638 | 20-22[1] | 38-49[2,16] |
| Elongation at Break | % | ASTM D638 | 6-12[1] | 4-7[2,16] |
| Flexural Modulus | MPa |
ASTM D790 |
781-987[3] | 2480-2520[1] |
| Flexural Stress at Break | % | ASTM D790 | 30-36[1] | 82-86[4] |
|
Flexural Elongation at Break |
MPa |
ASTM D790 |
>5[3,15] | >5[4,15] |
| IZOD Impact (Notched) | J/m |
|
N/A | 20-28[2] |
| Shore Hardness (3s) | D | ASTM D2240 | - | 83-85[10] |
Other Properties
| HDT at 0.455 MPa | ℃ | ASTM D648 | - | 66-76[5] |
| HDT at 1.82 MPa |
℃ |
ASTM D648 | - | 51-55[6] |
| Water Absorption (24hr) |
% |
ASTM D570 | - | 0.2-0.3[9] |
| Water Absorption (48hr) |
% |
ASTM D570 |
- | 0.3-0.4[9.1] |
| Water Absorption (72hr) | % |
ASTM D570 |
- | 0.4[9.1]-0.6[9] |
| Solid Density | g/cm ³ | ASTM D792 | 1.15[7] | 1.354[11] |
| Thermal Conductivity | W/(m*K) | ASTM 5930 | 0.204-0.206[12] | |
| Heat Capacity | J/(g*K) | ASTM 5930 | 1.211-1.231[12] |