LOCTITE® 3D IND405™ is a rigid, high strength, high elongation engineering material with outstanding impact resistance and excellent surface finish properties.
This stiff and durable high performance material is ideal for a wide variety of tools in the production floor, including manufacturing aids and final parts such as housing and consumer goods applications.
Parts can be printed with various DLP printers and machined, tapped or polished for final finish. Available in Black and Clear options.
Properties
| Mechanical Properties | Measure | Method | Green | Post Processed |
| Tensile Modulus | MPa | ASTM D638 | 897 ± 20 [1] | 1,434 ± 80 [2] |
| Tensile Stress at Yield | MPa | ASTM D638 | 25 ± 1 [1] | 44 ± 1 [2] |
| Elongation at Yield | % | ASTM D638 | 4.7 ± 0.2 [1] | 5.0 ± 0.3 [2] |
| Tensile Stress at Break | MPa |
ASTM D638 |
24 ± 1 [1] | 45 ± 2 [2] |
| Elongation at Break |
% |
ASTM D638 |
89 ± 9 [1] | 101 ± 11 [2] |
| Poisson’s Ratio | - |
ASTM D638 |
- | 0.44 ± 0.03 [14] |
| Flexural Modulus | MPa | ASTM D790 | 826 ± 27 [10] | 1383 ± 63 [10] |
| IZOD Impact (Notched) | J/m | ASTM D256 | - | 51 ± 4 [4] |
| Shore Hardness (3s) | D | ASTM D2240 | - | 76 [6] |
Other Properties
| HDT at 0.455 MPa | ℃ | ASTM D648 | - | 52.8 [3] |
| HDT at 1.82 MPa | ℃ | ASTM D256 | - | 43.3 [11] |
| Water Absorption (24 h) | % | ASTM D570 | - | 1.0 [5] |
| Solid Density |
g/cm³ |
ASTM D570 | 1.116 [7] | 1.121 [7] |
| Thermal Conductivity | W/(m*K) | ASTM D792 | - | 0.19 [8] |
| Heat Capacity | J/(g*K) | ASTM D5930 | - | 0.70 ± 0.07 [8] |
| CTE (-30℃ TO 45℃) | μm/(m*K) | ASTM D5930 | - | 98.47 [9] |
| Tg | ℃ | DIN 75200 | - | 97.8 [12] |
| Horizontal Burning Test | - | - | HB [13] |