Silver - 1.75mm PETG Filament - 1 kg Out of stock
Free Shipping within Canada and the USA on Orders >$99 CAD
Shipping via UPS to major cities and Canada Post for rural areas.
Average delivery time to Ontario and Quebec is 1 business day!
- Tags
- 1.75mm , metallic , silver , spo-disabled
SKU: StandardPETG175Silver1kg
It is the latest all-rounder co-polyester 3D filament which is made from a mixture of Glycerol and PET. All other 3D filaments were not specifically designed for printing objects in 3D; they were repurposed for 3D printing.
Their original purpose was something entirely different whereas PETG is that category of thermoplastics which is specially developed for 3D printing.
Its key features have subtle differences as compared to its counterparts, but they make all the difference. It produces little to no odor during printing and has real strength combined with enhanced flexibility and durability.
It has better layer adhesion for improved surface finish and has a higher melting point than PLA. Another advantage is that is comes approved by the FDA for food contact.
It is ideal for building mechanical parts and has more flexibility than ABS, PLA and even PET. The general temperature range for this thermoplastic is 220-235C. It does not require a heating bed, and there is minor shrinkage after cooling. It is eco-safe and can be properly recycled. It rarely warps and is known for its clarity and bridging properties.
| Physical | Nominal Value Unit | Test Method |
|---|---|---|
| Specific Gravity | 1.27 g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.20 % | ASTM D570 |
| Color b - Hunter4 | < 1.00 | ASTM E308 |
| Mechanical | Nominal Value Unit | Test Method |
| Tensile Strength Yield Break |
53.0 MPa 26.0 MPa |
ASTM D638 |
| Tensile Elongation5 Yield Break |
5.0 % 70 % |
ASTM D638 |
| Flexural Modulus | 2150 MPa | ASTM D790 |
| Flexural Strength 6 | 80.0 MPa | ASTM D790 |
| Impact | Nominal Value Unit | Test Method |
| Notched Izod Impact (23°C) | 90 J/m | ASTM D256 |
| Hardness | Nominal Value Unit | Test Method |
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Thermal | Nominal Value Unit | Test Method |
| Deflection Temperature Under Load 0.45 MPa, Unannealed 1.8 MPa, Unannealed |
74.0 °C 70.0 °C |
ASTM D648 |
| Vicat Softening Temperature | 83.0 °C | ASTM D15257 |
| Electrical | Nominal Value Unit | Test Method |
| Surface Resistivity | 1.0E+16 ohm | ASTM D257 |
| Volume Resistivity | 1.0E+15 ohm·cm | ASTM D257 |
| Dielectric Strength8 | 16 kV/mm | ASTM D149 |
| Dielectric Constant 1 kHz 1 MHz |
2.60 2.40 |
ASTM D150 |
| Dissipation Factor 1 kHz 1 MHz |
5.0E-3 0.023 |
ASTM D150 |
| Flammability | Nominal Value Unit | Test Method |
| Flame Rating 1.00 mm 1.50 mm 3.00 mm |
HB HB V-2 |
UL 94 |
| Optical | Nominal Value Unit | Test Method |
| Gloss (60°) | 159 | ASTM E308 |
| Refractive Index | 1.570 | ASTM D542 |
| Transmittance | 89.0 % | ASTM D1003 |
| Haze | < 1.0 % | ASTM D1003 |